Anti-Rust Metal Coating

Shielded Excellence: The Best Defense for Your Metals!

Consultation hotline00886-4-23286708

Online consultation

Product details

introduction

GPC specializes in the research and production of anti-rust coatings for hand tools, bathroom equipment, and related metallic products. Leveraging our profound technical expertise, we've successfully launched high-performance rust-preventative coatings suitable for a diverse range of substrates. Furthermore, our products are the preferred choice for many renowned hand tool brands in Europe and America, testifying to the trust and confidence they have in our advanced solutions.

Here's what we offer

1. Single-component clear coatings

2. Single-component colored coatings

the key features of our high-temperature metal coating

● Temperature Resilience:

Uncompromised protection even in extreme heat conditions.

● Strong Adhesion:

Stays firmly bonded to metal surfaces despite temperature fluctuations.

● Oxidation & Corrosion Resistance:

Guards against high-temperature oxidation and chemical damage.

● Durable & Abrasion-Resistant:

Retains its toughness and resists wear even in the heat.

● Quick Drying & Easy Application:

Efficiently coats metals without specialized tools.

Product Specification : Anti-Rust Metal Coating

Product Specifications	Main Component:	Thinner:302
Mixing Ratio	1 part	0.6-0.8parts
Baking Time	150℃*20minutes
Packaging Conditions	Packaging can proceed once the material has cooled down.

Physical Properties Test: Anti-Rust Metal Coating

Test Items		Test Conditions	Test Results
1	Adhesion	The sample is placed flat and scored both horizontally and vertically using a 100-grid knife. After cleaning the scored section, 3M#610 tape is applied over the grid. The tape is then pulled off at a 45° angle three times, resulting in a 5B adhesion rating.	5B
2	Hardness	Lay the test panel flat. Using the Mitsubishi Pencil Hardness Tester at a 500g load, the coating should exhibit a scratch-free surface with a hardness rating between H-2H.	No scratches
3	Acid Resistance	Upon immersion in 10% H2SO4 at 20±2℃ for 24 hours, the coating remains unaffected, with no noticeable softening, discoloration, bubbling, or decreased adhesion.	Appearance unchanged; 5B adhesion.
4	Alkali Resistance	Upon immersion in 10% NaOH at 20±2℃ for 24 hours, the coating remains unaffected, with no noticeable softening, discoloration, bubbling, or decreased adhesion.	Appearance unchanged; 5B adhesion.
5	Water Resistance	Immersed in pure water at 40±2℃ for 240 hours. After a 1-hour standing period post-immersion, the coating remains free from significant softening, discoloration, bubbling, or reduced adhesion.	Appearance unchanged; 5B adhesion.
6	salt spray resistance	Tested at 35℃ with 95% humidity using a 5% NaCl solution spray, the product showed no rust or discoloration on its surface after 48 hours in the salt spray environment.	Single-sided corrosion <2mm 5B adhesion.