Designed specifically for large-scale metal products, it offers a state-of-the-art alternative to traditional baking and curing processes, ensuring optimal finish and durability.
● Air Cure: Achieve perfect adhesion in just 10-30 minutes without external heating.
● Immaculate Surface: A lustrous, full-bodied coat amplifying the aesthetic of metal products.
● Robust & Decorative: Ensures high hardness and enhances the decorative effect.
● Superior Weather Resistance: Provides excellent resistance to weathering and chemicals while retaining gloss and color.
● Exceptional Adhesion & Durability: Engineered for longevity with outstanding mechanical properties.
● Primer Coating:
It lays a strong foundation, optimizing coating adhesion.
● Colored Coating:
It infuses products with vibrant, lasting shades.
● Clear Coating:
It adds a protective sheen, preserving the metal's innate shine and hue
Product Specifications |
Main Component: TP System |
Thinner: Air-drying thinner |
Mixing Ratio | 1 part | 1-1.5 parts |
Filter Mesh | Using a 200-300 mesh sieve | |
Spray Gun, Air Pressure | 3-4gf/cm2 | |
Film Thickness | 10±2um | |
Drying Method |
Air dry Note: For accelerated curing ( Bake at 60°C for 30 minutes) |
|
Packaging Conditions | After stabilizing at 60°C for 30 minutes, allow 3-5 hours for complete cooling before packaging. | |
Physical Testing Conditions | 60°C (2-4 hrs) or 80°C (1-2 hrs), stabilize for 4-6 hrs, then proceed with physical tests. | |
Suitable Substrates | Steel (Carbon, Stainless)、Aluminum、Copper & Copper Alloys (Bronze, Brass)、Zinc (Galvanized Steel)、Iron (Cast, Ductile) |
Test Items | Test Conditions | Test Results | |
1 | Adhesion | The sample is placed flat and scored both horizontally and vertically using a 100-grid knife. After cleaning the scored section, 3M#610 tape is applied over the grid. The tape is then pulled off at a 45° angle three times, resulting in a 5B adhesion rating. | 5B |
2 | Hardness | Sharpen a Mitsubishi H-grade pencil on sandpaper. Apply 500g weight and glide at a 45° angle from F to H. Ensure no scratches | F-H No scratches |
3 | Film Thickness | Electronic coating thickness gauge | 10±2um |
4 | Alcohol Resistance Test |
Rubbing Material: Cloth saturated with 99.5% alcohol. Load: 500g. Rubbing Distance: 3cm per cycle. Frequency: 30 cycles per minute. Criteria: The coating should exhibit no exposure of the underlying material (paint) after more than 200cycles. |
No substrate exposure observed |
5 | RCA Test | Using a 175g load and tape, the coating is rubbed 30 times without exposing the substrate (paint). | No substrate exposure observed |
6 | Boiling Water Resistance | It was submerged in an 80℃ water bath for 2 hours. The surface remains unchanged with a 5B pencil hardness test result. | No visible abnormalities, 5B hardness achieved. |
7 | High Temperature and Humidity Resistance | Exposed to 65℃ and 95% humidity for 120 hours, followed by a 6-hour recovery at room temperature. Post-examination shows no abnormalities with a 5B pencil hardness test result. | No visible abnormalities, 5B hardness achieved. |
8 | High Temperature Storage | Stored in a 70℃ environment for 48 hours, then allowed 4 hours to return to room temperature. Post-examination shows no abnormalities with a 5B pencil hardness test result. | No visible abnormalities, 5B hardness achieved. |
9 | Low Temperature Storage | Placed in a -40℃ environment for 48 hours, followed by a 4-hour recovery at room temperature. Post-examination shows no abnormalities with a 5B pencil hardness test result. | No visible abnormalities, 5B hardness achieved. |
10 | Thermal Shock Resistance | Alternated between 80℃ and -40℃, each temperature held for 1.5 hours with a 20-minute transition time, for a total of 20 cycles. Allowed 4 hours of recovery at room temperature. The surface should show no discoloration, blistering, peeling, shedding, or gloss variance. | No visible abnormalities, 5B hardness achieved. |
11 | Temperature and Humidity Cycling | Alternated between 65℃ at 95% humidity and -40℃, each condition held for 1.5 hours with a 20-minute transition time, for a total of 20 cycles. Allowed 4 hours of recovery at room temperature. The surface should show no discoloration, blistering, peeling, shedding, or gloss variance. | No visible abnormalities, 5B hardness achieved. |