Designed specifically for plastic products, our thermoplastic acrylic coatings not only provide a vibrant appearance but also boast excellent durability and eco-friendly attributes. Thanks to its unique one-component and air-curing property, the coating dries swiftly without the need for additional heating or complex curing processes.
Lay a solid foundation for your plastic products. Our primer coating not only optimizes adhesion but also ensures the longevity and integrity of the subsequent layers.
Infuse your plastic products with vibrant and enduring colors. Whether it's bright hues or subdued shades, our colored coatings capture them flawlessly
Add a protective layer of sheen while retaining the plastic's original shine and tint. This clear coating provides an extra shield for the plastic products, safeguarding against chemical corrosion and adverse weather conditions.
Product Specifications |
Main Component: TP System |
Thinner: Air-drying thinner |
Mixing Ratio | 1 part | 1-1.5 parts |
Filter Mesh | Using a 200-300 mesh sieve | |
Spray Gun, Air Pressure | 3-4gf/cm2 | |
Film Thickness | 10±2um | |
Drying Method |
Air dry Note: For accelerated curing ( Bake at 60°C for 30 minutes) |
|
Packaging Conditions | After stabilizing at 60°C for 30 minutes, allow 3-5 hours for complete cooling before packaging. | |
Physical Testing Conditions | 60°C (2-4 hrs) or 80°C (1-2 hrs), stabilize for 4-6 hrs, then proceed with physical tests. | |
Suitable Substrates | ABS, ABS+PC, PC, PS, PVC. |
Test Items | Test Conditions | Test Results | |
1 | Adhesion | The sample is placed flat and scored both horizontally and vertically using a 100-grid knife. After cleaning the scored section, 3M#610 tape is applied over the grid. The tape is then pulled off at a 45° angle three times, resulting in a 5B adhesion rating. | 5B |
2 | Hardness | Sharpen a Mitsubishi H-grade pencil on sandpaper. Apply 500g weight and glide at a 45° angle from F to H. Ensure no scratches | F-H No scratches |
3 | Film Thickness | Electronic coating thickness gauge | 10±2um |
4 | Alcohol Resistance Test |
Rubbing Material: Cloth saturated with 99.5% alcohol. Load: 500g. Rubbing Distance: 3cm per cycle. Frequency: 30 cycles per minute. Criteria: The coating should exhibit no exposure of the underlying material (paint) after more than 200cycles. |
No substrate exposure observed |
5 | RCA Test | Using a 175g load and tape, the coating is rubbed 30 times without exposing the substrate (paint). | No substrate exposure observed |
6 | Boiling Water Resistance | It was submerged in an 80℃ water bath for 2 hours. The surface remains unchanged with a 5B pencil hardness test result. | No visible abnormalities, 5B hardness achieved. |
7 | High Temperature and Humidity Resistance | Exposed to 65℃ and 95% humidity for 120 hours, followed by a 6-hour recovery at room temperature. Post-examination shows no abnormalities with a 5B pencil hardness test result. | No visible abnormalities, 5B hardness achieved. |
8 | High Temperature Storage | Stored in a 70℃ environment for 48 hours, then allowed 4 hours to return to room temperature. Post-examination shows no abnormalities with a 5B pencil hardness test result. | No visible abnormalities, 5B hardness achieved. |
9 | Low Temperature Storage | Placed in a -40℃ environment for 48 hours, followed by a 4-hour recovery at room temperature. Post-examination shows no abnormalities with a 5B pencil hardness test result. | No visible abnormalities, 5B hardness achieved. |
10 | Thermal Shock Resistance | Alternated between 80℃ and -40℃, each temperature held for 1.5 hours with a 20-minute transition time, for a total of 20 cycles. Allowed 4 hours of recovery at room temperature. The surface should show no discoloration, blistering, peeling, shedding, or gloss variance. | No visible abnormalities, 5B hardness achieved. |
11 | Temperature and Humidity Cycling | Alternated between 65℃ at 95% humidity and -40℃, each condition held for 1.5 hours with a 20-minute transition time, for a total of 20 cycles. Allowed 4 hours of recovery at room temperature. The surface should show no discoloration, blistering, peeling, shedding, or gloss variance. | No visible abnormalities, 5B hardness achieved. |