With 30 years of collaboration experience with leading bicycle manufacturers and nearly ten thousand
color trials and matches, we not only keep pace but lead the ever-evolving world of bicycle coatings. Our
partnerships with globally renowned bicycle factories highlight our unwavering dedication to paint quality,
expertise, and customer satisfaction. Our water-based, high-temperature, single-component bake paint,
crafted with expert precision, aims to provide both outstanding visual appeal and robust protection for
your bicycle.
●Primer Coating:
Crafted with distinct water-based ingredients, our primer provides a robust foundation for
specialty Formulated specifically to bond with diverse metal substrates and provide unparalleled
adhesion and resilience through the high-temperature baking process.
● Colored Coating:
Our ROHS-certified high-temperature water-based paint is renowned for its stability and vibrant colors
throughout the baking process.
●Clear Coating:
Maintains its brilliant shine and protective features throughout the high-temperature baking process.
Product Features
throughout the high-temperature baking process.
friendly.
during the baking process.
● Ease of Application: Simpler and more user-friendly compared to traditional coatings.
● Safety: Reduces the release of harmful chemicals during the heating process.
Product Specifications |
Main Component: Water-based AC system |
Diluent: Pure water |
Mixing Ratio |
1 part |
0.1-0.2 parts |
Filter Mesh |
Using a 300 / 400 mesh sieve |
|
Spray Gun, Air Pressure |
3-4gf/cm2 |
|
Film Thickness |
20±5um |
|
Baking Time |
120℃*20 minutes or 150℃*20 minutes |
|
Packaging Conditions |
Packaging can proceed once the material has cooled down. |
|
Physical Testing Conditions |
1. Standard testing conditions: 150℃ for 20 minutes. Once the material and coating have cooled down after being left at room temperature for 1-2 hours, physical property tests can be conducted.
2. Simulated environment test conditions: 150°C for 20 minutes, followed by letting it stand at room temperature for 24 hours before proceeding with the simulated environment test. |
|
Suitable Substrates |
Iron, Aluminum, Zinc Alloy. |
Test Items |
Test Conditions |
Test Results |
|
1 |
Adhesion |
The sample is placed flat and scored both horizontally and vertically using a 100-grid knife. After cleaning the scored section, 3M#610 tape is applied over the grid. The tape is then pulled off at a 45° angle three times, resulting in a 5B adhesion rating. |
5B |
2 |
Hardness |
Lay the test panel flat. Using the Mitsubishi Pencil Hardness Tester at a 500g load, the coating should exhibit a scratch-free surface with a hardness rating between F-H. |
No scratches |
3 |
Film Thickness |
Determined by film thickness gauge to be 20±5um (single coat of paint). |
20±5um |
4 |
Flexibility |
≤ 2mm without cracks |
no cracks |
5 |
Impact Test |
Φ1/2×500g×30cm No paint detachment |
No paint detachment |
6 |
Gloss Level |
Measured with a 60° gloss meter, the clear coat paint has a glossiness of over 97% |
Over 97% |
7 |
Electrical Resistance |
Conductivity Meter (0.05~2MΩ) |
|
8 |
Bleeding Resistance |
After affixing the color bleed test paper and baking it at 150°C for 20 minutes, no color bleeding was observed |
Non-bleeding |
9 |
QUV Resistance |
The clear coat undergoes a QUV test for 250 hours and other topcoats for more than 200 hours, with no fading. The gloss reduction is below 25%, excluding dyed paints. |
Non-fading
Loss of gloss <25% |
10 |
Corrosion Resistance |
Tested at 35℃ with 95% humidity using a 5% NaCl solution spray, the product showed no rust or discoloration on its surface after 480 hours in the salt spray environment. |
Single-sided corrosion <2mm
Adhesion meets standards. |
11 |
Humidity and Heat Test |
For the clear coat, after testing at 65℃ and 90% humidity for 24 hours, all properties remain unchanged. |
5B |
12 |
Solvent Resistance |
For the clear coat: Upon subjecting the sample to rubbing with xylene ten times, no alterations in hardness, bloom, softening, or glossiness were observed. |
OK |
Friendly to the environment, companion to metals.
Waterborne Coatings(High-temperature Baking Paint) Learn MoreWheels turn, Earth smiles.
Waterborne Coatings(High-temperature Baking Paint) Learn MoreLasting shine, never fades.
Waterborne Coatings(High-temperature Baking Paint) Learn More